1. WO2022160075 - BONDING PROCESS FOR HANDLE AND BODY OF MEDIUM-HIGH TEMPERATURE CERAMIC

Publication Number WO/2022/160075
Publication Date 04.08.2022
International Application No. PCT/CN2021/000194
International Filing Date 24.09.2021
IPC
C04B 33/24 2006.1
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
33Clay-wares
24Manufacture of porcelain or white ware
C04B 33/13 2006.1
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
33Clay-wares
02Preparing or treating the raw materials individually or as batches
13Compounding ingredients
C04B 35/622 2006.1
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
35Shaped ceramic products characterised by their composition; Ceramic compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
622Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
C04B 35/82 2006.1
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
35Shaped ceramic products characterised by their composition; Ceramic compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
71Ceramic products containing macroscopic reinforcing agents
78containing non-metallic materials
80Fibres, filaments, whiskers, platelets, or the like
82Asbestos; Glass; Fused silica
C04B 33/36 2006.1
CCHEMISTRY; METALLURGY
04CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
BLIME; MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
33Clay-wares
36Reinforced clay-wares
Applicants
  • 广东顺祥陶瓷有限公司 GUANGDONG SHUNXIANG PORCELAIN CO., LTD. [CN]/[CN]
Inventors
  • 许名传 XU, Mingchuan
  • 林伟河 LIN, Weihe
Agents
  • 汕头市潮睿专利事务有限公司 SHANTOU CHAORUI PATENT CO., LTD.
Priority Data
202110131769.730.01.2021CN
Publication Language Chinese (zh)
Filing Language Chinese (ZH)
Designated States
Title
(EN) BONDING PROCESS FOR HANDLE AND BODY OF MEDIUM-HIGH TEMPERATURE CERAMIC
(FR) PROCÉDÉ D’ADHÉSION DE POIGNÉE ET DE CORPS EN CÉRAMIQUE POUR TEMPÉRATURE MOYENNE À HAUTE
(ZH) 一种中高温陶瓷的器柄与器体的粘接工艺
Abstract
(EN) The present invention relates to a bonding process for a handle and a body of a medium-high temperature ceramic. According to the bonding process, asbestos fibers and a thickening agent are added in a sticking slurry; in a firing environment of a medium-high temperature ceramic, a ceramic blank is in a semi-molten state, the asbestos fibers are in a molten state, and the asbestos fibers respectively penetrate into the handle and the body from a connection; after the ceramic is out of a kiln and cooled, the asbestos fibers are present at the connection between the handle and the body and present on the handle and the body that are adjacent to the connection, and a bridging connection having a similar reinforced cement structure is formed, such that the handle and the body can be bonded firmly, the bending and tensile strengths of the connection between the handle and the body are improved, cracks would not formed at the connection between the handle and the body, and the connection is smooth and flat; moreover, after the asbestos fibers are uniformly mixed with a mud material, the thickening agent can improve the viscosity of the asbestos fibers in the mud material, such that the asbestos fibers are closely combined and integrated with the mud material, thus making the bonding between the handle and the body stable.
(FR) La présente invention concerne un procédé de liaison d'une poignée et d'un corps en céramique de température moyenne à haute. Selon le procédé d’adhésion, des fibres d'amiante et un agent épaississant sont ajoutés dans une bouillie collante ; dans un environnement de cuisson d'une céramique pour température moyenne à haute, une ébauche en céramique est à l'état semi-fondu, les fibres d'amiante sont à l'état fondu et les fibres d'amiante pénètrent, respectivement, dans la poignée et le corps à partir d'une jonction ; après que la céramique a été extraite d'un four et refroidie, les fibres d'amiante sont présentes au niveau de la jonction entre la poignée et le corps et présentes sur la poignée et le corps qui sont adjacents à la jonction, et une jonction de pontage ayant une structure similaire à du ciment renforcé est formée, de telle sorte que la poignée et le corps peuvent être amenées à adhérer fermement, les résistances à la flexion et à la traction de la jonction entre la poignée et le corps sont améliorées, des fissures ne seront pas formées au niveau de l’adhésion entre la poignée et le corps et la jonction est lisse et plate ; de plus, après que les fibres d'amiante sont mélangées de manière uniforme avec un matériau de boue, l'agent épaississant peut améliorer la viscosité des fibres d'amiante dans le matériau de boue, de telle sorte que les fibres d'amiante sont étroitement combinées et intégrées avec le matériau de boue, assurant une adhésion stable entre la poignée et le corps.
(ZH) 本发明涉及一种中高温陶瓷的器柄与器体的粘接工艺,这种粘接工艺在接头泥中添加了石棉纤维和增稠剂,在中高温陶瓷的烧制环境下,陶瓷坯料处于半融态,而石棉纤维处于熔化状态,石棉纤维从连接处分别渗透到器柄与器体上,当陶瓷出窑冷却后,在器柄与器体之间的连接处及其临近的器柄和器体上均存在有石棉纤维,形成具有类似钢筋水泥结构的桥接,使器柄与器体之间能够粘接得更加牢固,提高器柄与器体之间的连接处的抗弯和抗拉强度,避免器柄与器体之间的连接处出现裂痕,连接处更加光滑、平整;而石棉纤维均匀地与泥料混合后,增稠剂能够提高石棉纤维在泥料中粘度,使石棉纤维与泥料紧密结合、浑然一体,从而使器柄与器体之间的粘接更加稳定。